X8CrCoNiMo10-6
2014-09-11 10:18:17 Origin： Remark：0 Click：
Specifications X8CrCoNiMo10-8 datasheet, X8CrCoNiMo10-6 Chemical,X8CrCoNiMo10-6 properties from steelmaking, ESR, blooming, forging, rolling, heat treatment, straightened, ultrasonic test, cold working, machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL DATA SHEET - Grade X8CrCoNiMo10-6
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: 11Cr - 6Co - Fe base Superalloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.05～0.12
Si (％): 0.10～0.80
Mn (％): 0.20～1.35
P (％)≤: 0.025
S (％)≤: 0.020
Cr (％): 9.80～11.5
Ni (％): 0.20～1.20
Mo (％): 0.50～1.00
Co (％): 5.00～7.50
Si (％): 0.10～0.80
Mn (％): 0.20～1.35
P (％)≤: 0.025
S (％)≤: 0.020
Cr (％): 9.80～11.5
Ni (％): 0.20～1.20
Mo (％): 0.50～1.00
Co (％): 5.00～7.50
Nb (%): 0.20～0.60
V (%): 0.10～0.60
B (%): 0.005～0.015
N (%): ≤ 0.035
TYPICAL MECHANICAL PROPERTIES
Hot forming temperature /℃: 1100～850
Heat treatment temperature /℃ | annealing: 700~750
Heat treatment temperature /℃ | quenching or solution: 1160 ~ 1180 oil
Heat treatment temperature /℃ | tempering: 610~620
Heat treatment temperature /℃ | ageing: 620~650
Condition: heat treatment
Mechanical property under room temperature |σb/MPa: 980~1130
Mechanical property under room temperature |σs≥/MPa: 835
Mechanical property under room temperature |δ5≥(％): 15
Mechanical property under room temperature |Akv(DVM): 34
Heat stability temperature/℃: -
Non-scale temperature in air /℃: 700
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Final heat treatment - solution + Aged or Double aged.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Round bar (Diameter): 5.5 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：X8CrCoNiMo10-6