Technical specifications of high temperature alloy AF-1410 Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined.
TECHNICAL SPECIFICATION DATASHEET - Alloy AF-1410
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: American high temperature alloy and other special alloy
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.13 ~ 0.17
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.10
Phosphorus, P (％)≤: 0.008
Sulfur, S (％)≤: 0.005
Chromium, Cr (％): 1.80 ~ 2.20
Nickel, Ni (％): 9.50 ~ 10.5
Molybdenum, Mo (％): 0.90 ~ 1.10
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.10
Phosphorus, P (％)≤: 0.008
Sulfur, S (％)≤: 0.005
Chromium, Cr (％): 1.80 ~ 2.20
Nickel, Ni (％): 9.50 ~ 10.5
Molybdenum, Mo (％): 0.90 ~ 1.10
Cobalt, Co (%): 13.5 ~ 14.5
Tungsten, W (%): -
Aluminum, Al (%): ≤ 0.015
Copper, Cu (%): -
Aluminum, Al (%): ≤ 0.015
Copper, Cu (%): -
Titanium, Ti (%): ≤ 0.015
Nitrogen, N (%): ≤ 0.0015
Oxygen, O (%): ≤ 0.0015
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Heat treating fixture, Furnace muffle, Nuclear reactor.
Turbine engine parts - mechanical gears, gear shaft, main axis, blade.
Mechanical parts - bolt and nut, fastener.
Gas turbine, Turbine blade, Fuel nozzle.
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 10mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W60 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email: sales@ccsteels.com.
Hot search：AF-1410