NCF625
2016-08-22 12:26:38 Origin： Remark：0 Click：
Specifications NCF625 datasheet, NCF625 Chemical, NCF625 properties from Steelmaking, ESR melting, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - JIS G 4901 -1999 / JIS G4902 -1991.We also possess the advanced precision machining equipments for further processing.
TECHNICAL DATA SHEET - JIS NCF625
TECHNICAL SPECIFICATIONS - JIS G4901 -1999, JIS G 4902-1991
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - High temperature alloy and corrosion-resistant alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.10
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 20.0 ~ 23.0
Ni (％): ≥ 58.0
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 20.0 ~ 23.0
Ni (％): ≥ 58.0
Cu (％): -
Al (%): ≤ 0.40
Ti (%): ≤ 0.40
Fe (%): ≤ 5.00
Mo (%): 8.00 ~ 9.00
Nb + Ta (%): 3.15 ~ 4.15
MECHANICAL PROPERTIES, HEAT TREATMENT PRACTICE
Solution treated: ≥ 1090, rapid cooled
Annealed: ≥ 870, rapid cooled
Ageing treated: -
Condition: A
Tensile strength, σb/≥ MPa: 830
Yield strength, σ0.2/≥ MPa: 415
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Yield strength, σ0.2/≥ MPa: 415
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Suitable size /mm: 100
Tensile strength, σb/≥ MPa: 760
Yield strength, σ0.2/≥ MPa: 380
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Yield strength, σ0.2/≥ MPa: 380
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Suitable size /mm: 100 ~ 250
Condition: S
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 275
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Yield strength, σ0.2/≥ MPa: 275
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Suitable size /mm: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Heat treating fixture
Nuclear reactor
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Gas turbine, turbine blade
Fuel nozzle
Fuel nozzle
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT DESCRIPTION
The alloy is usually produced by EF + LF + VD + ESR, IFF + AOD + ESR, VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Final heat treatment - solution + age treated or double aged
The alloy is usually produced by EF + LF + VD + ESR, IFF + AOD + ESR, VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Final heat treatment - solution + age treated or double aged
FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Wire rod: 0.10 ~ 18mm
Sheet steel via cold rolled: T0.5 - 5.0 X W10 - 400 X L1000 - 2000mm or in coil form.
Steel strip via cold rolled: T0.1 - 3 X W5.0 - 200mm X C
Sheet steel via cold rolled: T0.5 - 5.0 X W10 - 400 X L1000 - 2000mm or in coil form.
Steel strip via cold rolled: T0.1 - 3 X W5.0 - 200mm X C
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：NCF625