ASTM B443 N06625
2016-09-21 11:40:56 Origin： Remark：0 Click：
Technical specification of American high temperature alloy N06625 Round bar, flat bar, plate Strip, Steelmaking, ESR melted, Hot forging, Hot rolling, Heat treatment, Ultrasonic test, Cold working.
TECHNICAL DATA SHEET - UNS N06625
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cr - Ni - Mo base superalloy
CHEMICAL COMPOSITION (mass weight %)
C (％): ≤ 0.10
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 20.0 ~ 23.0
Ni (％): 58.0 Min.
Mo (％): 8.00 ~ 10.0
Mn (％): ≤ 0.50
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 20.0 ~ 23.0
Ni (％): 58.0 Min.
Mo (％): 8.00 ~ 10.0
Cu (%): -
Ti (%): ≤ 0.40
Al (%): ≤ 0.40
Nb (%): 3.15 ~ 4.15
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Form: hot rolled plate
Condition: annealed, 871 Deg.
Tensile strength, σb/≥ MPa: 785
Yield strength, σ0.2/≥ MPa: 379
Elongation, δ ≥(％): 30.0
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HB: -
Condition: Solution treated, 1093 Deg.
Tensile strength,σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 270
Elongation, δ ≥(％): 30.0
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: 32
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Heat treating fixture, Furnace muffle, Nuclear reactor.
Turbine engine parts - mechanical gears, gear shaft, main axis, blade.
Mechanical parts - bolt and nut, fastener.
Gas turbine, Turbine blade, Fuel nozzle.
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W200 ~ 1000mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W200 ~ 1000mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com ) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com ) our resident team of qualified production engineers.
Previous page：INCOLOY 925
Last page：ASTM B443 N06219