ASTM B408 N08120
2016-09-24 15:03:17 Origin： Remark：0 Click：
Specifications N08120 Datasheet, N08120 Chemical, N08120 Properties from Steel making, ESR melted, Blooming, Forging, Hot rolling, Heat treat, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. Technical specification ASTM B408 - 2006.
TECHNICAL SPECIFICATION - ASTM B408 GR. N08120
TECHNICAL SPECIFICATION - ASTM B408 - 2006
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Nickel - Iron - Chromium alloy rod and bar
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.02 ~ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.035
S (％) ≤: 0.030
Cr (％): 23.0 ~ 27.0
Ni (％): 35.0 ~ 39.0
Mo (％): ≤ 2.50
Nb (%): 0.40 ~ 0.90
Ti (%): ≤ 0.20
Cu (%): ≤ 0.50
Al (%): ≤ 0.40
Al (%): ≤ 0.40
W (%): ≤ 2.50
Co (%): ≤ 3.00
Co (%): ≤ 3.00
N (%): 0.15 ~ 0.30
B (%): ≤ 0.010
Fe (%): Remainder
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Form: round bar
Condition: annealed, at 1177 Deg. min.
Tensile strength,σb/≥ MPa: 621
Yield strength, σ0.2/≥ MPa: 276
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: -
Fe (%): Remainder
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Form: round bar
Condition: annealed, at 1177 Deg. min.
Tensile strength,σb/≥ MPa: 621
Yield strength, σ0.2/≥ MPa: 276
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: -
Service temperature: above 593 Deg.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
These materials must stand up to high heat, extreme oxidation potential and recycling.
AVAILABLE FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
These materials must stand up to high heat, extreme oxidation potential and recycling.
AVAILABLE FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：31NiCr14 & 1.5755
Last page：Haynes HR-120 / N08120