Incoloy 800H / N08810
2016-09-27 12:05:02 Origin： Remark：0 Click：
Material standard specification for Nickel-Iron-Chromium alloy rod and bar Incoloy 800H / N08810 data sheet, Incoloy 800H / N08810 Chemical compositions, Incoloy 800H mechanical properties from Steel making, ESR melted, Blooming, Forging, Hot rolling, N08810 Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. Technical specification ASTM B408 - 2006.
TECHNICAL SPECIFICATION - INCOLOY 800H & N08810
TECHNICAL SPECIFICATION: ASTM B408 - 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Nickel - Iron - Chromium alloy rod and bar
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.05 ~ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.045
S (％) ≤: 0.015
Cr (％): 19.0 ~ 23.0
Ni (％): 30.0 ~ 35.0
Mo (％): -
Ti (%): 0.15 ~ 0.60
Cu (%): ≤ 0.75
Al (%): 0.15 ~ 0.60
Al (%): 0.15 ~ 0.60
Fe (%): 39.5 Min.
MECHANICAL PROPERTIES
Form: rod and bar
Condition: cold worked and hot worked, annealed, at 1121 Deg. min.
Tensile strength,σb/≥ MPa: 450
Yield strength, σ0.2/≥ MPa: 170
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: -
MECHANICAL PROPERTIES
Form: rod and bar
Condition: cold worked and hot worked, annealed, at 1121 Deg. min.
Tensile strength,σb/≥ MPa: 450
Yield strength, σ0.2/≥ MPa: 170
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: -
Service temperature: above 593 Deg.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
These materials must stand up to high heat, extreme oxidation potential and recycling.
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: lh.steel@hotmail.com
Hot search：Incoloy 800H/N08810
Previous page：ASTM B408 N08810
Last page：ASTM B408 N08811