Incoloy 800HT & N08811
2016-09-28 13:19:16 Origin： Remark：0 Click：
Incoloy 800HT/N08811 datasheet, Incoloy 800HT/N08811 Chemical compositions,Incoloy 800HT mechanical properties from Steel making, ESR melted, Blooming,Incoloy 800HT/N08811 Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. Technical specification ASTM B408 - 2006.
MATERIAL TECHNICAL STANDARD - INCOLOY 800HT & N08811
TECHNICAL SPECIFICATION: ASTM B408 - 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Nickel - Iron - Chromium alloy rod and bar
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.06 ~ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.045
S (％) ≤: 0.015
Cr (％): 19.0 ~ 23.0
Ni (％): 30.0 ~ 35.0
Mo (％): -
Ti (%): 0.15 ~ 0.60
Cu (%): ≤ 0.75
Al (%): 0.15 ~ 0.60
Al (%): 0.15 ~ 0.60
Al + Ti (%): 0.85 ~ 1.20
Fe (%): 39.5 Min.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: rod and bar
Condition: cold worked and hot worked, annealed, at 1150 Deg. min.
Tensile strength,σb/≥ MPa: 450
Yield strength, σ0.2/≥ MPa: 170
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: rod and bar
Condition: cold worked and hot worked, annealed, at 1150 Deg. min.
Tensile strength,σb/≥ MPa: 450
Yield strength, σ0.2/≥ MPa: 170
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness | HRC: -
Service temperature: above 593 Deg.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry:
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry:
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Gas turbine
Turbine blade
Fuel nozzle
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Gas turbine
Turbine blade
Fuel nozzle
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
FORMS AND SHAPES
Round bar (Diameter): 0.50mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：Incoloy 800HT & N08811
Previous page：ASTM B408 N08811
Last page：ASTM B408 N08890