X6CrNiMo17-13
2014-09-12 09:22:39 Origin： Remark：0 Click：
Description X6CrNiMo17-13 datasheet, X6CrNiMo17-13 Chemical, X6CrNiMo17-13 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET of Creep-resisting Steel - DIN X6CrNiMo17-13
MATERIAL CATEGORY - Austenitic creep-resisting steels
MATERIAL SPECIFICATIONS - DIN 17442, 17744, DIN EN 10302, 10095, EN 10088-1
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.04 ~ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.015
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.015
N (%): ≤ 0.11
Al (%): -
Cr (％): 16.5 ～ 18.5
Mo (％): 2.00 ～ 2.50
Mo (％): 2.00 ～ 2.50
Nb (%): -
Ni (％): 10.0 ～ 13.0
Ti (%): -
V (%): -
W (%): -
B (％): 0.0015 ~ 0.0050
B (％): 0.0015 ~ 0.0050
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution treatment
Tensile strength, σb/MPa: 550~750
Tensile strength, σb/MPa: 550~750
Yield strength, σs≥/MPa: 260
Elongation, δ5≥(％): 35.0
Elongation, δ5≥(％): 35.0
Non-scale temperature in Air ℃: -
MANUFACTURING TECHNOLOGY - SMELTING
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality, it should be smelt via technology of vacuum refining and external refining.
Heat resistant steel is generally smelt in electric arc furnace or induction furnace. For higher quality, it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：X6CrNiMo17-13