ASTM B564 N04400
2017-02-16 11:29:39 Origin： Remark：0 Click：
Technical specifications of ASTM B564-04 Nickel alloy forgings N04400 Round bar, Flat bar, ESR melted, Hot forging / rolling, Heat treatment
TECHNICAL DATA SHEET - ASTM B564-04 Grade N04400
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Nickel - Copper Alloy
KEY CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.30
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): -
Nickel, Ni (％): 63.0 min.
Molybdenum, Mo (％): -
Copper, Cu (%): 28.0 ~ 34.0
Cobalt, Co (%): -
Tungsten, W (%): -
Ferrum, Fe (%): ≤ 2.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, Rm ≥ MPa: 483
Yield strength, Rp0.2 ≥ MPa: 172
Elonghation, A5 ≥ (％): 35.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar & Disc (diameter): 5.5 to 650mm
Square bar / Flat bar: 6 to 500mm
Heavy/middle plate via hot rolled: T6 - 200 X W10 - 1500 X Lmm
Sheet steel via cold rolled: T0.5 - 6 X W60 - 1000mm X L1000 - 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Tungsten, W (%): -
Ferrum, Fe (%): ≤ 2.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, Rm ≥ MPa: 483
Yield strength, Rp0.2 ≥ MPa: 172
Elonghation, A5 ≥ (％): 35.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar & Disc (diameter): 5.5 to 650mm
Square bar / Flat bar: 6 to 500mm
Heavy/middle plate via hot rolled: T6 - 200 X W10 - 1500 X Lmm
Sheet steel via cold rolled: T0.5 - 6 X W60 - 1000mm X L1000 - 2000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.