ASTM B564 N06600
2017-02-17 09:49:26 Origin： Remark：0 Click：
Specifications N06600 Datasheet, Inventory N06600 Chemical, Suppliers N06600 Properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM B564-04 Grade UNS N06600
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ni - Cr - Fe Alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): ≤ 0.50
Mn (％): ≤ 1.00
P (％) ≤: 0.025
S (％) ≤: 0.015
Cr (％): 14.0 ~ 17.0
Ni (％): 72.0 min.
Mo (％): -
Cu (%): ≤ 0.50
Co (%): -
W (%): -
Fe (%): 6.00 ~ 10.0
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 552
Yield strength, σ0.2/≥ MPa: 241
Elonghation, δ ≥(％): 30.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 300mm X W60 - 1200mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
W (%): -
Fe (%): 6.00 ~ 10.0
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 552
Yield strength, σ0.2/≥ MPa: 241
Elonghation, δ ≥(％): 30.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 300mm X W60 - 1200mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：ASTM B564 N04400
Last page：ASTM B564 N06690