ASTM B564 N06625
2017-02-25 09:19:24 Origin： Remark：0 Click：
Description N06625 Sheet, Inventory N06625 Forgings, Suppliers N06625 Round bars Properties from Steelmaking, ESR melted, Blooming, Hot forging/rolling, Heat treat, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
RAW MATERIAL SPECIFICATIONS - Grade N06625
MATERIAL CATEGORY - Ni-Cr-Mo-Nb high alloy steel
MATERIAL SPECIFICATIONS- ASTM B564
MATERIAL SPECIFICATIONS- ASTM B564
MELTING PROCESS - VIM + Consumable electrode remelted steel
H S CODE For Customs - 72201100 / 72202030 / 72221100
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (Mass Weight - %)
C (％): ≤ 0.10H S CODE For Customs - 72201100 / 72202030 / 72221100
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (Mass Weight - %)
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 20.0 ~ 23.0
Ni (％): 58.0 min.
Mo (％): 8.00 ~ 10.0
Cu (%): -
Mn (％): ≤ 0.50
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 20.0 ~ 23.0
Ni (％): 58.0 min.
Mo (％): 8.00 ~ 10.0
Cu (%): -
Al (%): ≤ 0.40
Ti (%): ≤ 0.40
Ce (%): -
Zr (%): -
Y (%): -
Nb (%): 3.15 ~ 4.15
Co (%): -
V (%): -
N (%): -
B (%): -
W (%): -
W (%): -
Ta (%): -
Fe (%): 5.00 max.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 827
Yield strength, σ0.2/≥ MPa: 414
Elonghation, δ ≥(％): 30.0
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 300mm X W60 - 1500mm X L1000 ~ 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.3 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Fe (%): 5.00 max.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 827
Yield strength, σ0.2/≥ MPa: 414
Elonghation, δ ≥(％): 30.0
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 300mm X W60 - 1500mm X L1000 ~ 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.3 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：ASTM B564 N08811
Last page：NF EN X6CrMoNb17-1