N08031
2017-03-10 08:43:14 Origin： Remark：0 Click：
Technical specifications of ASTM B564-04 Nickel alloy forgings Grade N08031 Round bar, Flat bar, plate ESR melted, Hot rolling, Heat treatment, Straightening, Cold machined.
TECHNICAL DATA SHEET - ASTM B564-04 Grade UNS N08031
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: low-carbon-Ni-Fe-Cr-Mo-Cu Alloy
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.015
Silicon, Si (％): ≤ 0.30
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 26.0 ~ 28.0
Nickel, Ni (％): 30.0 ~ 32.0
Molybdenum, Mo (％): 6.00 ~ 7.00
Copper, Cu (%): 1.00 ~ 1.40
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 26.0 ~ 28.0
Nickel, Ni (％): 30.0 ~ 32.0
Molybdenum, Mo (％): 6.00 ~ 7.00
Copper, Cu (%): 1.00 ~ 1.40
Nitrogen, N (%): 0.15 ~ 0.25
Ferrum, Fe (%): Balance
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 650
Yield strength, σ0.2/≥ MPa: 276
Elonghation, δ ≥(％): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 650
Yield strength, σ0.2/≥ MPa: 276
Elonghation, δ ≥(％): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：UNS N06219
Last page：NAS 325N