Specifications N06230 Datasheet, Inventory N06230 Chemical, Stocklist N06230 Properties from Steelmaking, ESR melted, Blooming, Forging, UNS N06230 Hot rolling, Heat treat, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM B564-04 Grade UNS N06230
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ni-Cr-W-Mo Alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.05 ~ 0.15
Si (％): 0.25 ~ 0.75
Mn (％): 0.30 ~ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 20.0 ~ 24.0
Ni (％): Balance
Mo (％): 1.00 ~ 3.00
Cu (%): -
Mn (％): 0.30 ~ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 20.0 ~ 24.0
Ni (％): Balance
Mo (％): 1.00 ~ 3.00
Cu (%): -
Al (%): 0.20 ~ 0.50
Ti (%): -
Ce (%): -
Zr (%): -
Y (%): -
Nb (%): -
Co (%): ≤ 5.00
V (%): -
N (%): -
B (%): ≤ 0.015
La (%): 0.005 ~ 0.050
W (%): 13.0 ~ 15.0
W (%): 13.0 ~ 15.0
Ta (%): -
Fe (%): 3.0 max.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 758
Yield strength, σ0.2/≥ MPa: 310
Elonghation, δ ≥(％): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
SHAPES & DIMENSIONS
Round bar (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Fe (%): 3.0 max.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 758
Yield strength, σ0.2/≥ MPa: 310
Elonghation, δ ≥(％): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
SHAPES & DIMENSIONS
Round bar (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：N06230
Previous page：SKC3
Last page：Haynes alloy 230