Technical specifications of ASTM B564-04 Nickel alloy forgings Grade UNS N10629 datasheet, UNS N10629 Chemical compositions, UNS N10629 mechanical properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, UNS N10629 Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM B564-04 Grade UNS N10629
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ni-Mo Alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.010
Si (％): ≤ 0.50
Mn (％): ≤ 1.50
P (％) ≤: 0.040
S (％) ≤: 0.010
Cr (％): 0.50 ~ 1.50
Ni (％): Balance
Mo (％): 26.0 ~ 30.0
Cu (%): ≤ 0.50
Mn (％): ≤ 1.50
P (％) ≤: 0.040
S (％) ≤: 0.010
Cr (％): 0.50 ~ 1.50
Ni (％): Balance
Mo (％): 26.0 ~ 30.0
Cu (%): ≤ 0.50
Al (%): 0.10 ~ 0.50
Ti (%): -
Ce (%): -
Zr (%): -
Y (%): -
Nb (%): -
Co (%): ≤ 2.50
V (%): -
N (%): -
B (%): -
La (%): -
W (%): -
W (%): -
Ta (%): -
Fe (%): 1.0 ~ 6.0
MECHANICAL PROPERTIES
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 760
Yield strength, σ0.2/≥ MPa: 350
Elonghation, δ ≥(％): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Fe (%): 1.0 ~ 6.0
MECHANICAL PROPERTIES
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 760
Yield strength, σ0.2/≥ MPa: 350
Elonghation, δ ≥(％): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.