B166 type N06617
2017-04-03 14:05:37 Origin： Remark：0 Click：
Description N06617 Ex-stock, Suppliers N06617 Round bar, Inventory N06617 Forgigns Properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treat, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM B166 Grade UNS N06617
TECHNICAL SPECIFICATION: ASTM B166-2011
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.05 ~ 0.15
C (％): 0.05 ~ 0.15
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.020
S (％) ≤: 0.015
Cr (％): 20.0 ~ 24.0
Ni (％): 44.5 min.
Mo (％): 8.00 ~ 10.0
Mn (％): ≤ 1.00
P (％) ≤: 0.020
S (％) ≤: 0.015
Cr (％): 20.0 ~ 24.0
Ni (％): 44.5 min.
Mo (％): 8.00 ~ 10.0
Cu (%): ≤ 0.50
Al (%): 0.80 ~ 1.50
Ti (%): ≤ 0.60
Zr (%): -
Y (%): -
Nb (%): -
Co (%): 10.0 ~ 15.0
N (%): -
B (%): ≤ 0.006
W (%): -
Fe (%): 3.0 max.
TYPICAL MECHANICAL PROPERTIES
Condition: Cold/ Hot worked, annealed
Tensile strength, σb/≥ MPa: 655
TYPICAL MECHANICAL PROPERTIES
Condition: Cold/ Hot worked, annealed
Tensile strength, σb/≥ MPa: 655
Yield strength, σ0.2/≥ MPa: 240
Elonghation, δ ≥(％): 35.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 500mm
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.25 ~ 3.00, W5.0 ~ 500, in coil form
Forging piece: stepped shafts with discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Forging piece: stepped shafts with discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：C120E3U
Last page：AMS 6263G / SAE 9315