B166 type N06690
2017-04-06 09:09:24 Origin： Remark：0 Click：
Technical specification of ASTM B166-2011 Nickel-Chromium-Iron alloy type N06690 datasheet,type N06690 Chemical compositions, type N06690 mechanical properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM B166 Grade UNS N06690
TECHNICAL SPECIFICATION: ASTM B166-2011
MATERIAL CATEGORY: Ni-Cr-Fe Alloy
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
C (％): ≤ 0.05
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 27.0 ~ 31.0
Ni (％): 58.0 min.
Mo (％): -
Mn (％): ≤ 0.50
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 27.0 ~ 31.0
Ni (％): 58.0 min.
Mo (％): -
Cu (%): ≤ 0.50
Al (%): -
Ti (%): -
Zr (%): -
Y (%): -
Nb (%): -
Co (%): -
N (%): -
B (%): -
W (%): -
Fe (%): 7.00 ~ 11.0
MECHANICAL PROPERTIES
Condition: Cold/ Hot worked, annealed
Tensile strength, σb/≥ MPa: 725
MECHANICAL PROPERTIES
Condition: Cold/ Hot worked, annealed
Tensile strength, σb/≥ MPa: 725
Yield strength, σ0.2/≥ MPa: 550
Elonghation, δ ≥(％): 12.0
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.25 ~ 3.00, W5.0 ~ 500, in coil form
Forging piece: stepped shafts with discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Forging piece: stepped shafts with discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: lh.steel@hotmail.com