AISI 633
2017-05-16 08:50:03 Origin： Remark：0 Click：
Specifications AISI 633 datasheet, AISI 633 Chemical, AISI 633 Properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treat, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
MATERIAL TECHNICAL DATA SHEET - AISI 633
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Martensitic high-tensile superalloy & Precipitation hardening steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.07 ~ 0.11
Si (％): ≤ 0.50
Mn (％): 0.50 ~ 1.25
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 16.0 ~ 17.0
Ni (％): 4.00 ~ 5.00
Mo (％): 2.50 ~ 3.20
Mn (％): 0.50 ~ 1.25
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 16.0 ~ 17.0
Ni (％): 4.00 ~ 5.00
Mo (％): 2.50 ~ 3.20
N (%): 0.07 ~ 0.13
Co (%): -
W (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Tensile strength, σb/≥ MPa: 1380
Yield strength, σ0.2/≥ MPa: 580 ~ 620
Elonghation, δ ≥(％): 12.0
Reduction of area, ф ≥ (％): -
Hardness | HB: HRC30 max.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 300mm X W70 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 600mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 300mm X W70 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 600mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com.
Previous page：NF HS6-5-2-5
Last page：AM 350