Alloy 52/N14052
2017-05-29 10:34:44 Origin： Remark：0 Click：
Technical specifications of American high temperature alloys Alloy 52/N14052 datasheet, Alloy 52/ N14052 Chemical compositions, Alloy 52 /N14052 mechanical properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL SPECIFICATION & DATASHEET - Alloy 52 & N14052
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: American high temperature alloy and other special alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): ≤ 0.30
Mn (％): ≤ 0.60
P (％)≤: 0.025
S (％)≤: 0.025
Cr (％): ≤ 0.25
Ni (％): 50.5 NOM
Mo (％): -
Co (%): ≤ 0.50
W (%): -
Al (%): ≤ 0.10
Cu (%): -
Ti (%): -
Fe (%): Remainder
MECHANICAL PROPERTY AT ROOM TEMP.
Condition: annealed
Ultimate Tensile Strength: 78 KSI nom (536 MPa nom)
Yield Strength: 35 KSI nom (240 MPa nom) Elongation: 30% nom
Hardness: Rb 73 nom
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 800mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): ≤ 0.30
Mn (％): ≤ 0.60
P (％)≤: 0.025
S (％)≤: 0.025
Cr (％): ≤ 0.25
Ni (％): 50.5 NOM
Mo (％): -
Co (%): ≤ 0.50
W (%): -
Al (%): ≤ 0.10
Cu (%): -
Ti (%): -
Fe (%): Remainder
MECHANICAL PROPERTY AT ROOM TEMP.
Condition: annealed
Ultimate Tensile Strength: 78 KSI nom (536 MPa nom)
Yield Strength: 35 KSI nom (240 MPa nom) Elongation: 30% nom
Hardness: Rb 73 nom
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 800mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: lh.steel@hotmail.com
You also can reach our sales production for detailed quotation via E-mail: sales@ccsteels.com