Aquamet 18
2017-06-12 08:50:31 Origin： Remark：0 Click：
Stocklist Aquamet 18 Shaft, Specifications Aquamet 18 Inventory Aquamet 18 Properties from Steelmaking, ESR melted, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATASHEET - Grade Aquamet 18
SPECIAL MELTING PROCESS - BEF + AOD / + ESR
MATERIAL CATEGORY - Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE - Austenitic stainless steel series
HS Code For Customs - 72221100 / 72221900 / 72222000
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176,
CHEMICAL COMPOSITION (Mass weight - % )
C (％): ≤ 0.15
Si (％): ≤ 1.00
Mn (％): 11.0 ~ 14.0
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.5 ~ 19.0
Ni (％): 0.50 ~ 2.50
Mo (％): -
Ti (%): -
N (％): 0.20 ~ 0.45
Si (％): ≤ 1.00
Mn (％): 11.0 ~ 14.0
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 16.5 ~ 19.0
Ni (％): 0.50 ~ 2.50
Mo (％): -
Ti (%): -
N (％): 0.20 ~ 0.45
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of thermal treatment: + AT ( solution annealing treated )
Tensile strength, σb/≥ MPa: 827
Yield strength, σ0.2/≥ MPa: 621
Elonghation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 45.0
Hardness | HB: - Impact absorbing power Akv≥/J : -
Tensile strength, σb/≥ MPa: 827
Yield strength, σ0.2/≥ MPa: 621
Elonghation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 45.0
Hardness | HB: - Impact absorbing power Akv≥/J : -
PRODUCT DESCRIPTION
The alloy is usually produced by EAF AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged
The alloy is usually produced by EAF AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T60 - 400mm X W70 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com