Aquamet 19
2017-06-13 12:47:12 Origin： Remark：0 Click：
Stocklist Aquamet 19 Datasheet, Shaft Aquamet 19 Chemical, Inventory Aquamet 19 Properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATASHEET - Grade Aquamet 19
SPECIAL MELTING PROCESS - BEF + AOD / + ESR
MATERIAL CATEGORY - Stainless steel round bar, wire rod, and semi-finished products
STEEL TYPE - Austenitic stainless steel series
HS Code For Customs - 72221100 / 72221900 / 72222000
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176,
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 18.0 ~ 20.0
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 18.0 ~ 20.0
Ni (％): 8.00 ~ 10.5
Mo (％): -
Cu (%): -
Ti (%): -
N (％): 0.20 ~ 0.45
Mo (％): -
Cu (%): -
Ti (%): -
N (％): 0.20 ~ 0.45
Fe (%): Remainder
SHORT BRIEF - AQUAMET 19 is a modified Type 304 stainless steel that is fully austenitic, non-magnetic and strengthened by nitrogen addition, with corrosion resistance better than Type 304 stainless steel.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 827
Yield strength, σ0.2/≥ MPa: 724
Elonghation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 55.0
Hardness | HB:
Yield strength, σ0.2/≥ MPa: 724
Elonghation, δ ≥(％): 20.0
Reduction of area, ф ≥ (％): 55.0
Hardness | HB:
PRODUCT DESCRIPTION
The alloy is usually produced by EAF AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged
The alloy is usually produced by EAF AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + aged
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy / middle plate via hot rolled: T60 - 400mm X W70 - 1500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com