Stocklist Chrome core 13 Datasheet, Inventory Chrome core 13 Chemical, Supplier Chrome core 13 Properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL DATA SHEET - Grade Chrome core 13
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL TYPE - Cr - Fe martensitic stainless steel
CHEMICAL COMPOSITION ( Mass weight %)
C (％): ≤ 0.030
Si (％): 0.70 ~ 1.80
Mn (％): 0.20 ~ 0.70
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 12.5 ~ 13.5
C (％): ≤ 0.030
Si (％): 0.70 ~ 1.80
Mn (％): 0.20 ~ 0.70
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 12.5 ~ 13.5
Ni (％): -
Mo (％): 0.20 ~ 0.50
Mo (％): 0.20 ~ 0.50
N (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 425
Yield strength, σ0.2/≥ MPa: 228
Elongation, δ ≥(％): 45.0
Reduction of area, ф ≥ (％): 55
Hardness | HB: -
Yield strength, σ0.2/≥ MPa: 228
Elongation, δ ≥(％): 45.0
Reduction of area, ф ≥ (％): 55
Hardness | HB: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our qualified production engineers.
E-mail: sales@ccsteels.com
If you meet further on any technical enquiry or help, pleased to EMAIL our qualified production engineers.
E-mail: sales@ccsteels.com
Previous page：Chrome core 12-FM
Last page：DTD713