Chrome core 18-FM is a Free machining high content of Chromium 18.0% Ferritic Stainless Steel, Normal forms in Round bar, Flat bar, Plate Produced from Steelmaking, Blooming, Hot forging, rolling, Heat treatment, Cold machined.
MATERIAL TECHNICAL DATA SHEET - Grade Chrome core 18-FM
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL TYPE: Cr - Fe Alloy steel
CHEMICAL COMPOSITION (mass weight %)
C (％): 0.10 ~ 0.30
Si (％): 0.70 ~ 1.20
Mn (％): 0.30 ~ 0.75
P (％)≤: 0.020
S (％)≤: 0.20 ~ 0.40
Cr (％): 15.0 ~ 19.0
C (％): 0.10 ~ 0.30
Si (％): 0.70 ~ 1.20
Mn (％): 0.30 ~ 0.75
P (％)≤: 0.020
S (％)≤: 0.20 ~ 0.40
Cr (％): 15.0 ~ 19.0
Ni (％): ≤ 0.50
Mo (％): 1.50 ~ 2.00
Nb/Ta (%): 0.20 ~ 0.40
Mo (％): 1.50 ~ 2.00
Nb/Ta (%): 0.20 ~ 0.40
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 517
Yield strength, σ0.2/≥ MPa: 345
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): 60
Hardness | HB: -
Yield strength, σ0.2/≥ MPa: 345
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): 60
Hardness | HB: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
SHAPES AND DIMENSIONS
Round bar (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers. E-mail: sales@ccsteels.com
Previous page：27MnB4/ 1.5536
Last page：X2Cr17