Technical specifications of American high temperature alloys CMN datasheet, Grade CMN Chemical compositions, CMN mechanical properties from Steelmaking, ESR melted, Blooming, Forging, CMN Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL DATA SHEET - Grade CMN
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL TYPE: Cr - Fe alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.60 ~ 0.70
Si (％): ≤ 0.35
Mn (％): 11.0 ~ 13.0
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 24.0 ~ 26.0
C (％): 0.60 ~ 0.70
Si (％): ≤ 0.35
Mn (％): 11.0 ~ 13.0
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 24.0 ~ 26.0
Ni (％): -
Mo (％): -
Co (%): -
Co (%): -
W (%): -
Al (%): -
Ti (%): -
Al (%): -
Ti (%): -
B (%):
Fe (%): Remainder
N (%): 0.40 ~ 0.50
MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 720
Yield strength, σ0.2/≥ MPa: 300
Elongation, δ ≥(％): 50.0
Reduction of area, ф ≥ (％): -
Hardness | HB: -
Yield strength, σ0.2/≥ MPa: 300
Elongation, δ ≥(％): 50.0
Reduction of area, ф ≥ (％): -
Hardness | HB: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers. - Email: lh.steel@hotmail.com
You also can reach our sales dept via E-mail: sales@ccsteels.com
Hot search：CMN
Previous page：Chromel
Last page：30MoB1 / 1.5408