Croloy 16-6PH
2017-08-09 08:46:53 Origin： Remark：0 Click：
Technical specifications of Croloy 16-6PH Round bar, flat bar, ESR melted, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or machined.
MATERIAL TECHNICAL DATA SHEET - Grade Croloy 16-6PH
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL TYPE: Cr - Ni - Al - Ti Precipitation hardening alloy
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.025 ~ 0.045
Silicon, Si (％): ≤ 0.50
Carbon, C (％): 0.025 ~ 0.045
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.70 ~ 0.90
Phosphorus, P (％) ≤: 0.025
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 15.0 ~ 16.0
Chromium, Cr (％): 15.0 ~ 16.0
Nickel, Ni (％): 7.00 ~ 8.00
Molybdenum, Mo (％): -
Cobalt, Co (%): -
Cobalt, Co (%): -
Tungsten, W (%): -
Aluminium, Al (%): 0.25 ~ 0.40
Aluminium, Al (%): 0.25 ~ 0.40
Copper, Cu (%): -
Titanium, Ti (%): 0.30 ~ 0.50
Titanium, Ti (%): 0.30 ~ 0.50
MECHANICAL PROPERTIES AT ROOM TEMP.
Tensile strength, σb/≥ MPa: 825
Yield strength, σ0.2/≥ MPa: 515
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Hardness | HBW: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Hardness | HBW: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar / Disc (Diameter): 5.50mm to 650mm
Square bar / Flat bar: 3mm to 450mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar / Disc (Diameter): 5.50mm to 650mm
Square bar / Flat bar: 3mm to 450mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers. - Email:
sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers. - Email:
sales@ccsteels.com