Technical specifications of Ferralium 255 Round bar, flat bar, sheet, and forgings Steelmaking, ESR melted, Hot forging, Hot rolling, Heat treatment, 100% Ultrasonic flaw detection test, Cold machined.
TECHNICAL DATA SHEET - Grade Ferralium 255
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cr - Ni - Mo - Cu - Fe base alloy
CHEMICAL COMPOSITION (mass weight %)
C (％): ≤ 0.025
Si (％): ≤ 0.70
Mn (％): 0.80 ~ 1.20
P (％)≤: 0.025
C (％): ≤ 0.025
Si (％): ≤ 0.70
Mn (％): 0.80 ~ 1.20
P (％)≤: 0.025
S (％)≤: 0.020
Cr (％): 24.5 ~ 26.5
Cr (％): 24.5 ~ 26.5
Ni (％): 5.50 ~ 6.50
Mo (％): 3.10 ~ 3.80
Co (%): -
Co (%): -
W (%): -
Al (%): -
Al (%): -
Cu (%): 1.50 ~ 2.00
Ti (%): -
Ti (%): -
Fe (%): remainder
N (%): 0.22 ~ 0.33
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 790
Yield strength, σ0.2/≥ MPa: 586
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): 50.0
Hardness | HBW: 220 ~ 270
Reduction of area, ф ≥ (％): 50.0
Hardness | HBW: 220 ~ 270
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.50 ~ 500mm
Square bar / Flat bar: 3 ~ 450mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.50 ~ 500mm
Square bar / Flat bar: 3 ~ 450mm
Wire rod (Diameter): 0.10 ~ 13mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.
Email: sales@ccsteels.com.
Previous page：T11362
Last page：Alloy 255/SD40