1.3912
2018-05-07 13:11:32 Origin： Remark：0 Click：
Specifications 1.3912 data sheet, 1.3912 Chemical, 1.3912 Properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3
TECHNICAL DATA SHEET - 1.3912
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.10
Si (％): ≤ 0.35
Mn (％): ≤ 0.60
P (％)≤: 0.025
S (％)≤: 0.025
Cr (％): ≤ 0.50
Ni (％): 35.0 ~ 38.0
Mo (％): ≤ 0.50
Si (％): ≤ 0.35
Mn (％): ≤ 0.60
P (％)≤: 0.025
S (％)≤: 0.025
Cr (％): ≤ 0.50
Ni (％): 35.0 ~ 38.0
Mo (％): ≤ 0.50
Co (%): ≤ 1.00
Fe (％): Remainder
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 490
Yield strength, σ0.2/≥ MPa: 310
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 140
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: 140
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 800mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.