Technical specifications of American standards ageing hardened steel alloy AMS 6514 data sheet, AMS 6514 Chemical composition,AMS 6514 mechanical properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. Technical specification - AMS 6512. We also possess the advanced precision machining equipments for further processing. Please just let us know what you inquire.
TECHNICAL DATA SHEET - AMS 6514
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: maraging stainless steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 0.10
Mn (％): ≤ 0.10
P (％)≤: 0.010
S (％)≤: 0.010
Cr (％): ≤ 0.50
Ni (％): 18.0 ~ 19.0
Mo (％): 4.60 ~ 5.20
Si (％): ≤ 0.10
Mn (％): ≤ 0.10
P (％)≤: 0.010
S (％)≤: 0.010
Cr (％): ≤ 0.50
Ni (％): 18.0 ~ 19.0
Mo (％): 4.60 ~ 5.20
Co (%): 8.30 ~ 9.50
Ti (%): 0.60 ~ 0.80
Other (％): Al 0.05 ~ 0.15, Cu ≤ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: after maraging heat treated
Tensile Strength, σb/≥ MPa: 1070
Yield Strength, σ0.2/ MPa: 870
Elongation, δ ≥(％): 14.0
Elongation, δ ≥(％): 14.0
Reduction of Area, ф ≥ (％): -
Hardness | HRC: 36 max..
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment
Steel strip via cold rolled: Thickness 0.1 - 3 mm X Width 5 - 200mm X L (or in coil form)
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - solution treatment
Steel strip via cold rolled: Thickness 0.1 - 3 mm X Width 5 - 200mm X L (or in coil form)
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: lh.steel@hotmail.com
Previous page：X2NiCoMo18-9-5 / 1.6358
Last page：AMS 6515