Technical specifications of American high temperature alloy Incoloy 832 datasheet,Incoloy alloy 832 Chemical compositions, Incoloy 832 mechanical properties from Steelmaking, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Incoloy 832
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cr-Ni-Mo Fe base Superalloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
C (％): ≤ 0.05
Si (％): ≤ 1.20
Mn (％): ≤ 0.80
P (％)≤: 0.030
Mn (％): ≤ 0.80
P (％)≤: 0.030
S (％)≤: 0.005
Cr (％): 19.5 ~ 21.0
Cr (％): 19.5 ~ 21.0
Ni (％): 8.75 ~ 15.5
Mo (％): 0.30 ~ 0.55
Co (%): -
Co (%): -
W (%): -
Al (%): 0.10 ~ 0.30
Al (%): 0.10 ~ 0.30
Cu (%): ≤ 0.75
Ti (%): 0.15 ~ 0.60
Fe (% ): Balance
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 762
Yield strength, σ0.2/MPa: 364
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
FORMS AND SHAPES
Round bar (Diameter): 5.50 ~ 450 mm
Square bar / Flat bar: 3 ~ 350 mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
FORMS AND SHAPES
Round bar (Diameter): 5.50 ~ 450 mm
Square bar / Flat bar: 3 ~ 350 mm
Wire rod (Diameter): 0.30 ~ 12mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.