Z6CNU17-04
2019-11-02 15:50:38 Origin： Remark：0 Click：
Material technical specifications of NF A35-574 -1990 hot rolled stainless steel bars & wire rod, NF Z6CNU17-04 datasheet, Z6CNU17-04 Chemical compositions, Z6CNU17-04 mechanical properties from Steelmaking, ESR melting, Hot blooming, UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A35-574 - 1990. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Alloy NF Z6CNU17-04
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Hot rolled stainless steel round bar and wire rod
Technical standards: NF A35-574 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 0.75
MATERIAL CATEGORY: Hot rolled stainless steel round bar and wire rod
Technical standards: NF A35-574 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 0.75
Mn (％): ≤ 2.00
P (％)≤: 0.030
S (％)≤: 0.020
Cr (％): 15.0 ~ 17.5
S (％)≤: 0.020
Cr (％): 15.0 ~ 17.5
Ni (%): 3.00 ~ 5.00
Mo (％): ≤ 0.50
Cu (%): 3.00 ~ 5.00
Nb + Ta (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution annealed + Aged H1050
Tensile strength, TS, σb/≥ MPa: 950 ~ 1150
Yield strength, YS, σ0.2/≥ MPa: 800
Elongation, EL, δ ≥(％): 10.0
Yield strength, YS, σ0.2/≥ MPa: 800
Elongation, EL, δ ≥(％): 10.0
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: 365
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD + VD, AOD + EF / EAF + VD, followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment or based on the buyer's special requirements.
The alloy is usually produced by BEF + AOD + VD, AOD + EF / EAF + VD, followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment or based on the buyer's special requirements.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter): 0.50mm to 16mm
Strip: T0.20~3.0 X W8.0~650mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Other sizes can be supplied to meet specific requirements.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, please EMAIL our qualified production engineers. E-mail: lh.steel@hotmail.com
If you meet further on any technical enquiry, please EMAIL our qualified production engineers. E-mail: lh.steel@hotmail.com