AMS 5656 Specifications, AMS 5656 Ex-stock, Forging AMS 5656 bar plate machined, AMS 5656 Exporters from Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test,
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - AMS 5656
MATERIAL CATEGORY: Austenitic Stainless Steel bar
Technical standards: ASTM A276. A580
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.00
Mn (％): 8.00 ~ 10.0
P (％)≤: 0.060
S (％)≤: 0.030
Cr (％): 19.0 ~ 21.0
Ni (％): 5.50 ~ 7.50
Mo (％): -
N (％): 0.15 ~ 0.40
Si (％): ≤ 1.00
Mn (％): 8.00 ~ 10.0
P (％)≤: 0.060
S (％)≤: 0.030
Cr (％): 19.0 ~ 21.0
Ni (％): 5.50 ~ 7.50
Mo (％): -
N (％): 0.15 ~ 0.40
Tensile strength, σb/MPa: 655 min.
Yield strength, σ0.2/MPa: 330 min.
Elongation, δ (％): 30 min.
Reduction of area, ф (％): -
Elongation, δ (％): 30 min.
Reduction of area, ф (％): -
Hardness (HBW): -
Hardness | HRB: -
Cold bending property: None
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / EAF VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
The alloy is usually produced by BEF + AOD / EAF VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, E-mail: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.