ASTM 403Cb Specifications, ASTM 403Cb Chemical, ASTM 403Cb Bar, Wire rod, Steelmaking, ESR, Hot blooming, Hot forging, Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
Material Specifications - ASTM A565
TECHNICAL DATA SHEET - ASTM 403Cb
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL SPECIFICATIONS: ASTM A565
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.13 ~ 0.18
Si (％): ≤ 0.50
Mn (％): 0.40 ~ 0.60
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 11.5 ~ 13.0
Ni (％): ≤ 0.50
Mo (％): ≤ 0.20
Si (％): ≤ 0.50
Mn (％): 0.40 ~ 0.60
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 11.5 ~ 13.0
Ni (％): ≤ 0.50
Mo (％): ≤ 0.20
Nb (%): 0.15 ~ 0.45
Al (％): ≤ 0.05
Al (％): ≤ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: HT 1136℃~1163℃, ≥677℃ X 2h tempered
Tensile strength, σb ≥/MPa: 795
Yield strength, σ0.2 ≥/MPa: 515
Yield strength, σ0.2 ≥/MPa: 515
Elontation, δ ≥(％): 15.0
Reduction of area, ф ≥(％): 50.0
Hardness | HRS: ≤ 277
Reduction of area, ф ≥(％): 50.0
Hardness | HRS: ≤ 277
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / Quenched and tempered.
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / Quenched and tempered.