Nitronic 32
2020-04-30 13:22:00 Origin： Remark：0 Click：
Nitronic 32 Suppliers, Nitronic 32 Specifications, Nitronic 32 Properties from Steelmaking, ESR melted, Hot Blooming, Hot forging & Rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power.100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Nitronic 32
MATERIAL CATEGORY: Austenitic Stainless Steel
Technical standards: ASTM A276, A580
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): ≤ 1.00
Mn (％): 11.0 ~ 14.0
P (％)≤: 0.060
S (％)≤: 0.030
Cr (％): 16.5 ~ 19.5
Ni (％): 0.50 ~ 2.50
Mo (％): -
N (％): 0.20 ~ O.45
Si (％): ≤ 1.00
Mn (％): 11.0 ~ 14.0
P (％)≤: 0.060
S (％)≤: 0.030
Cr (％): 16.5 ~ 19.5
Ni (％): 0.50 ~ 2.50
Mo (％): -
N (％): 0.20 ~ O.45
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/MPa: 760 min.
Yield strength, σ0.2/MPa: 420 min.
Elongation, δ (％): 50 min.
Reduction of area, ф (％): 70.0
Elongation, δ (％): 50 min.
Reduction of area, ф (％): 70.0
Hardness (HBW): -
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by BEF + AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.
Round bar / Wire rod (Diameter1): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1300mm, with wall thickness ranging from 15 to 350 mm.