AMS 5354 Ex-stock Coils, AMS 5354 Chemical, AMS 5354 Strip forging Bar rod steelmaking, ESR, Blooming, Hot forging & Hot rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL SPECIFICATION DATASHEET - AMS 5354
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic high content chromium round bar and forge piece
MATERIAL SPECIFICATIONS: AMS 5354
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.15 ~ 0.20
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 12.0 ~ 14.0
Ni (％): 1.80 ~ 2.20
Mo (％): ≤ 0.50
W (％): 2.50 ~ 3.50
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 12.0 ~ 14.0
Ni (％): 1.80 ~ 2.20
Mo (％): ≤ 0.50
W (％): 2.50 ~ 3.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: Annealed
Tensile strength, σb ≥/MPa: -
Yield strength, σ0.2 ≥/MPa:-
Yield strength, σ0.2 ≥/MPa:-
Elongation, δ ≥(％): -
Reduction of area, ф ≥(％): -
Hardness | HBW: ≤ 311
Reduction of area, ф ≥(％): -
Hardness | HBW: ≤ 311
Condition of heat treatment: HT 981℃ ~ 1080℃ air or oil cooled, ≥620℃ X 2H, two times tempered
Tensile strength, σb ≥/MPa: 965
Yield strength, σ0.2 ≥/MPa: 760
Yield strength, σ0.2 ≥/MPa: 760
Elongation, δ ≥(％): 15.0
Reduction of area, ф ≥(％): 45.0
Hardness | HBW: 302 ~ 352
Reduction of area, ф ≥(％): 45.0
Hardness | HBW: 302 ~ 352
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD followed by electroslag refining ESR & VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and Tempered
The alloy is usually produced by BEF + AOD followed by electroslag refining ESR & VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and Tempered
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip via cold rolled: T0.5 - 3mm X W5 - 300mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com