Descriptions Z5CNU15.05 datasheet,Z5CNU15-05 Chemical,Z5CNU15-05 Properties Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MARTENSITIC STEEL DATA SHEET - Grade NF Z5CNU15.05
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: 15Cr - 5Ni - 4Cu Martensitic stainless
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.0 ~ 15.5
Ni (％): 3.50 ~ 5.50
Mo (％): —
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.0 ~ 15.5
Ni (％): 3.50 ~ 5.50
Mo (％): —
Cu (％): 2.50 ~ 4.50
Nb+Ta (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, forge piece
Condition: H900
Tensile strength, σb/MPa: 1310
Yield strength, σ0.2/MPa: 1170
Elongation, δ (％): 10.0
Reduction of area, ψ (％): 35
Harndess: HRC: ≥ 40
Condition: H900
Tensile strength, σb/MPa: 1310
Yield strength, σ0.2/MPa: 1170
Elongation, δ (％): 10.0
Reduction of area, ψ (％): 35
Harndess: HRC: ≥ 40
Form: Bar, forge piece
Condition: H925
Condition: H925
Tensile strength, σb/MPa: 1170
Yield strength, σ0.2/MPa: 1070
Elongation, δ (％): L-10.0
Reduction of area, ψ (％): L-38.0
Hardness HRC: ≥ 38
Yield strength, σ0.2/MPa: 1070
Elongation, δ (％): L-10.0
Reduction of area, ψ (％): L-38.0
Hardness HRC: ≥ 38
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment + aged
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 3 ~ 350mm
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 3 ~ 350mm
Rolled plate: 10 ~ 400 X 60 ~ 1200 X length
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form).
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form).
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.