STR661
2020-07-28 12:11:08 Origin： Remark：0 Click：
Specifications STR661 heat treatment, STR661 datasheet, Alloy STR 661 chemical Forging Bar machined, STR661 Exporters Technical specifications - KS D3731 - 2002 / 2007. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATASHEET - Grade STR 661
TECHNICAL SPECIFICATIONS: KS D3731 - 2002/2007
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resistant stainless steel bar and plate
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.08 ~ 0.16
Si (％): ≤ 1.50
Mn (％): 1.00 ~ 2.00
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 20.0 ~ 22.5
Ni (％): 19.0 ~ 21.0
Mo (%): 2.50 ~ 3.50
N (%): 0.10 ~ 0.20
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resistant stainless steel bar and plate
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.08 ~ 0.16
Si (％): ≤ 1.50
Mn (％): 1.00 ~ 2.00
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 20.0 ~ 22.5
Ni (％): 19.0 ~ 21.0
Mo (%): 2.50 ~ 3.50
N (%): 0.10 ~ 0.20
W (%): 2.00 ~ 3.00
Co (%): 18.5 ~ 21.0
Nb (%): 0.75 ~ 1.25
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated 1130 ~ 1200 Deg.C, Ageing 780 ~ 830 X 4h, air cooling or slow cooling.
Tensile strength, σb/ ≥ MPa: 755
Yield strength, σ0.2/ ≥ MPa: 343
Elongation, δ (％) ≥: 30.0
Reduction of area, ф (％) ≥: 30.0
Hardness ≤ (HBW): 192 Min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated 1130 ~ 1200 Deg.C, Ageing 780 ~ 830 X 4h, air cooling or slow cooling.
Tensile strength, σb/ ≥ MPa: 755
Yield strength, σ0.2/ ≥ MPa: 343
Elongation, δ (％) ≥: 30.0
Reduction of area, ф (％) ≥: 30.0
Hardness ≤ (HBW): 192 Min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：STR661
Previous page：STR 661
Last page：ASTM A182 Gr.F310H