Round bar AMS 5719 Stock, AMS 5719 Hexagon bar, Flat bar AMS 5719 Plate Turbine Blade Steel ESR refined, Hot forging, Hot rolling, Heat treatment.
AEROSPACE MATERIAL SPECIFICATION - Grade AMS 5719
TECHNICAL SPECIFICATIONS - AMS 5719C
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.08 ~ 0.13
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 11.0 ~ 12.5
Molybdenum, Mo (％): 1.50 ~ 2.00
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 11.0 ~ 12.5
Molybdenum, Mo (％): 1.50 ~ 2.00
Nickel, Ni (%): 2.00 ~ 3.00
Vanadium, V (％): 0.25 ~ 0.40
Nitrogen, N (%): 0.01 ~ 0.05
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb≥ /MPa: 1100
Yield strength, σs≥ /Mpa: 860
Elongation, δ5 ≥(%): 12.0
Hardness HBW: 341 ~ 375
Yield strength, σs≥ /Mpa: 860
Elongation, δ5 ≥(%): 12.0
Hardness HBW: 341 ~ 375
Hardness HBS: 310 max in annealed condition
HEAT TREATMENT PRACTICE
Annealed: 691° C (+/-11) for 6 hours min followed by air cool
Hardened:1052° C (+/-) for 30 mins followed by oil quench
1st Tempered: 560-590° C for 1 hour min followed by air cool
2nd Tempered: 538-560° C for 3 hours min followed by air cool
Annealed: 691° C (+/-11) for 6 hours min followed by air cool
Hardened:1052° C (+/-) for 30 mins followed by oil quench
1st Tempered: 560-590° C for 1 hour min followed by air cool
2nd Tempered: 538-560° C for 3 hours min followed by air cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS AND DIMENSIONS
Round bar & Disc (diameter): 5.5 ~ 800mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 4 ~ 800mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar.
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS AND DIMENSIONS
Round bar & Disc (diameter): 5.5 ~ 800mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 4 ~ 800mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
Previous page：N07722
Last page：Inconel 722