Inventory AMS 5585 Specifications, Suppliers AMS 5585 Datasheet, Chemical Property AMS 5585 Stockholder from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL STANDARD - Grade AMS 5585
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5585G
HS Code for Customs - 72221100 / 72221900 / 72223000
Techncial Specifications - AMS 5585G
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report- issued by TUV - SGS - BV
Chemical compositions (Mass weight %)
Chemical compositions (Mass weight %)
C (％): 0.08 ~ 0.16
Si (％): ≤ 1.00
Mn (％): 1.00 ~ 2.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 22.0 ~ 22.5
Ni (％): 19.0 ~ 21.0
Si (％): ≤ 1.00
Mn (％): 1.00 ~ 2.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 22.0 ~ 22.5
Ni (％): 19.0 ~ 21.0
Co (%): 18.5 ~ 21.0
Mo (％): 2.50 ~ 3.50
Mo (％): 2.50 ~ 3.50
Nb (%): 0.75 ~ 1.25
N (％): 0.10 ~ 0.20
N (％): 0.10 ~ 0.20
Cu (%): ≤ 0.50
Ta (%): ≤ 0.05
Fe (%): Remainder
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bars, plate, tubings and forgings
Form: Bars, plate, tubings and forgings
Heat treatment condition: solution annealing treated
Tensile strength, σb/MPa: 689
Yield strength, σ0.2/MPa: -
Elongation, δ(％): 35.0
Reduction of area, ф (％): -
Elongation, δ(％): 35.0
Reduction of area, ф (％): -
Hardness | HRW: -
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD, VOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 620mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 300mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD, VOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 620mm
Wire rod: 0.5mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 300mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.