Description NCF80A Stocklist, Inventory NCF80A Round bar, Suppliers NCF80A Stcoklist Property Technical specifications - KS D3531 - 2003. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - Grade NCF80A
Technical Specifications - KS D3531 - 1992/2003
Official Test Certificate - issued by TUV - SGS - BV
Material Category - Heat resistant stainless steel & Superalloy
Chemical Composition (Mass Weight - %)
C (％): 0.04 ~ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 18.0 ~ 21.0
Ni (％): Remainder
Official Test Certificate - issued by TUV - SGS - BV
Material Category - Heat resistant stainless steel & Superalloy
Chemical Composition (Mass Weight - %)
C (％): 0.04 ~ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 18.0 ~ 21.0
Ni (％): Remainder
Cu (％): ≤ 1.00
Al (%): 1.00 ~ 1.80
Ti (%): 1.80 ~ 2.70
Fe (%): ≤ 1.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution annealing, 1050 ~ 1100 Deg. C min. rapid colling.
Condition: Solution annealing, 1050 ~ 1100 Deg. C min. rapid colling.
Aged 690 ~ 710 Deg. C 16h, air cooling.
Tensile strength, σb/ ≥ MPa: 1000
Yield strength, σ0.2/ ≥ MPa: 600
Elongation, δ (％) ≥: 20.0
Reduction of area, ф (％) ≥: -
Hardness under solution anneal ≤ (HBW): 269
Yield strength, σ0.2/ ≥ MPa: 600
Elongation, δ (％) ≥: 20.0
Reduction of area, ф (％) ≥: -
Hardness under solution anneal ≤ (HBW): 269
MELTING PROCESS
The alloy is usually produced by AOD / EAF / VIM, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 400mm
Wire rod (Diameter): 0.15 ~ 13mm
Flat bar (Thickness X Width): 4 ~ 300 X 15 ~ 600mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
The alloy is usually produced by AOD / EAF / VIM, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 400mm
Wire rod (Diameter): 0.15 ~ 13mm
Flat bar (Thickness X Width): 4 ~ 300 X 15 ~ 600mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com.
If you meet further on any technical inquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com.
Hot search：NCF80A