Description Aermet 100 Round bars, Ex-stock Aermet 100 Shaft, Inventory Aermet 100 Stocklist Properties from Steelmaking VIM ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined.
TECHNICAL DATA SHEET - Grade Aermet 100
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
SPECIAL MELTING PROCESS - VIM + ESR / VAR
MATERIAL CATEGORY - Stainless steel round bar, wire rod, and semi-finished products
HS Code For Customs - 72221100 / 72221900 / 72222000
MATERIAL CATEGORY - Nickel-Cobalt base Superalloy
CHEMICAL COMPOSITION (mass weight %)
C (％): 0.21 ~ 0.25
Si (％): ≤ 0.10
Mn (％): ≤ 0.10
P (％) ≤: 0.010
S (％) ≤: 0.008
Cr (％): 2.90 ~ 3.30
Ni (％): 11.0 ~ 12.0
Mo (%): 1.10 ~ 1.30
Co (％): 13.0 ~ 14.0
Al (%): ≤ 0.015
Cu: (%): -
Ti (%): ≤ 0.015
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
SPECIAL MELTING PROCESS - VIM + ESR / VAR
MATERIAL CATEGORY - Stainless steel round bar, wire rod, and semi-finished products
HS Code For Customs - 72221100 / 72221900 / 72222000
MATERIAL CATEGORY - Nickel-Cobalt base Superalloy
CHEMICAL COMPOSITION (mass weight %)
C (％): 0.21 ~ 0.25
Si (％): ≤ 0.10
Mn (％): ≤ 0.10
P (％) ≤: 0.010
S (％) ≤: 0.008
Cr (％): 2.90 ~ 3.30
Ni (％): 11.0 ~ 12.0
Mo (%): 1.10 ~ 1.30
Co (％): 13.0 ~ 14.0
Al (%): ≤ 0.015
Cu: (%): -
Ti (%): ≤ 0.015
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 1900
Yield strength, σ0.2/MPa: 1600
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥ (％): 55.0
Hardness via annealed treated /HBW: 365 max.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 300mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE AND SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry or help, pleased to EMAIL our qualified production engineers TODAY, Email: sales@ccsteels.com.
Tensile strength, σb/≥ MPa: 1900
Yield strength, σ0.2/MPa: 1600
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥ (％): 55.0
Hardness via annealed treated /HBW: 365 max.
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.5 ~ 300mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE AND SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry or help, pleased to EMAIL our qualified production engineers TODAY, Email: sales@ccsteels.com.
Previous page：FE-PM 3504
Last page：AMS 6532