Inconel X750 Steel, round bar, flat bar, plate has been used typically for parts, Inconel X750 bolts, turbine blades, and turbine seals, requiring oxidation resistance and high strength at 677 to 816 °C.
MATERIAL TECHNICAL DATASHEET - Grade Inconel X750
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5668K
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.08
Manganese, Mn (％): ≤ 1.00
Silicon, Si (％): ≤ 0.50
Phosphorus, P (％)≤: 0.015
Sulfur, S (％)≤: 0.010
Chromium, Cr (％): 14.0 ~ 17.0
Nickel, Ni (％): 70.0 Min.
Molybdenum, Mo (%): -
Niobium, Nb (%): 0.70 ~ 1.20
Titanium, Ti (%): 2.25 ~ 2.75
Aluminum, Al (%): 0.40 ~ 1.00
Coppper, Cu (%): ≤ 0.50
Tantalum, Ta (%): ≤ 0.05
Cobalt, Co (%): ≤ 1.00
Ferrum, Fe (%): 5.00 ~ 9.00
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5668K
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.08
Manganese, Mn (％): ≤ 1.00
Silicon, Si (％): ≤ 0.50
Phosphorus, P (％)≤: 0.015
Sulfur, S (％)≤: 0.010
Chromium, Cr (％): 14.0 ~ 17.0
Nickel, Ni (％): 70.0 Min.
Molybdenum, Mo (%): -
Niobium, Nb (%): 0.70 ~ 1.20
Titanium, Ti (%): 2.25 ~ 2.75
Aluminum, Al (%): 0.40 ~ 1.00
Coppper, Cu (%): ≤ 0.50
Tantalum, Ta (%): ≤ 0.05
Cobalt, Co (%): ≤ 1.00
Ferrum, Fe (%): 5.00 ~ 9.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Shapes: bars, forgings and rings.
Heat treatment practice: solution heat treated by heating to 1149 °C ± 14 °C,
holding at heat for 2 to 4 hours, and cooling in air.
Tensile strength, σb/MPa: 965
Yield strength, σ0.2/MPa: 552
Elongation, δ(％): 8.0
Reduction of area, ф (％): 8.0
Hardness under hot finished condition | HBW: +
Hardness under precipitation heat treatment condition | HBW: 262 ~ 341
AVAILABLE SHAPES & DIMENSIONS
Round bar (Diameter): 5.5 to 500mm
Square bar / Flat bar (Thickness X width): 10 to 610mm
Wire rod (Diameter): 1.0 to 11.0mm
Steel strip: THK0.5 ~ 3.0, width 10 ~ 220mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Tensile strength, σb/MPa: 965
Yield strength, σ0.2/MPa: 552
Elongation, δ(％): 8.0
Reduction of area, ф (％): 8.0
Hardness under hot finished condition | HBW: +
Hardness under precipitation heat treatment condition | HBW: 262 ~ 341
AVAILABLE SHAPES & DIMENSIONS
Round bar (Diameter): 5.5 to 500mm
Square bar / Flat bar (Thickness X width): 10 to 610mm
Wire rod (Diameter): 1.0 to 11.0mm
Steel strip: THK0.5 ~ 3.0, width 10 ~ 220mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Previous page：AMS 5667 & N07750 Round bar, Plate, Forgings
Last page：AMS 5668