Nickel Alloy AMS 5682 Round bar, flat bar, Corrosion and Heat Resistant Coating, Rods and Wire 78Ni - 20Cr Austenitic stainless steel.
MATERIAL TECHNICAL DATASHEET - Grade AMS 5682
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5682D
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): 0.15 ~ 0.30
Manganese, Mn (％): 0.60 ~ 1.00
Silicon, Si (％): ≤ 0.30
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5682D
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): 0.15 ~ 0.30
Manganese, Mn (％): 0.60 ~ 1.00
Silicon, Si (％): ≤ 0.30
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 19.0 ~ 21.0
Nickel, Ni (％): remainder.
Cobalt, Co (%): ≤ 1.00
Ferrum, Fe (%): ≤ 1.0
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Shapes: wire, bars
Tensile strength, σb/MPa: 515
Yield strength, σ0.2/MPa: 205
Elongation, δ(％): 40.0
Reduction of area, ф (％): -
Hardness under hot finished condition | HBW: 201 max.
Hardness under precipitation heat treatment condition | HBR: -
RELEVANT STANDARDS FOR REFERENCE
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring both corrosion and oxidation resistance.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 19.0 ~ 21.0
Nickel, Ni (％): remainder.
Cobalt, Co (%): ≤ 1.00
Ferrum, Fe (%): ≤ 1.0
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Shapes: wire, bars
Tensile strength, σb/MPa: 515
Yield strength, σ0.2/MPa: 205
Elongation, δ(％): 40.0
Reduction of area, ф (％): -
Hardness under hot finished condition | HBW: 201 max.
Hardness under precipitation heat treatment condition | HBR: -
RELEVANT STANDARDS FOR REFERENCE
AMS 2261 Tolerances, Metric, Nickel, Nickel Alloy, and Cobalt Alloy Bars, Rods, and Wire.
AMS 2269 Chemical Check Analysis Limits, Wrought Nickel Alloys and Cobalt Alloys
AMS 2371 Quality Assurance Sampling and Testing, Corrosion and Heat Resistant Steels and Alloys, Wrought Products and Forging Stock.
AMS 2806 Identification, Bars, Wire, Mechanical Tubing, and Extrusions, Carbon and Alloy Steels and Corrosion and Heat Resistant Steels and Alloys
ASTM A370 Mechanical Testing of Steel Products.MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring both corrosion and oxidation resistance.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Previous page：S34781
Last page：AMS 5683 Welding Wire Rod