42.0% Nickel base Austenitic type N09706 Round bar, flat bar, plate N09706 ESR melted, Blooming, Hot forging / Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working.
TECHNICAL DATASHEET - Grade N09706
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5701D
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.06
Manganese, Mn (％): ≤ 0.35
Silicon, Si (％): ≤ 0.35
Phosphorus, P (％)≤: 0.020
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 14.5 ~ 17.5
Nickel, Ni (％): 39.0 ~ 44.0
Niobium, Nb (%): 2.50 ~ 3.30
Copper, Cu (%): ≤ 0.30
Titanium, Ti (%): 1.50 ~ 2.00
Aluminum, Al (%): ≤ 0.40
Boron, B (%): ≤ 0.006
Ferrum, Fe (%): remainder.
MECHANICAL PROPERTIES AT ROOM TEMP.
Condition: 980 ℃ quenched 1 hour, air cooling, 718 ℃ 8 hour furnace cooling to 620℃, air cooling.,
Tensile strength, σb/MPa: 1167
Yield strength, σ0.2/MPa: 892
Elongation, δ(％): 12.0
Reduction of area, ф (％): 15.0
Hardness under hot finished condition | HBW: 285 max.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 550mm
Wire rod (diameter): 0.50 ~ 5.5mm
Square bar / Flat bar (Thickness X Width): 10 to 600mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：N09706