Steel round bar AMS 5741 Forgings Corrosion and Heat resistant 13.5Cr - 26Ni - I.8Mo - 3.0Ti - 0.02B Consumable Electrode Vacuum Melted Solution Stabilization and Precipitation Heat Treated
TECHNICAL DATA SHEET - AMS 5741
Material Category - Aerospace Material Steel Series
Techncial Specifications - AMS 5741D
HS Code for Customs - 72221100 / 72221900 / 72223000
Official Test Report - issued by TUV - SGS - BV
TYPICAL CHEMICAL ELEMENTS (mass fraction - %)
Carbon, C (％): ≤ 0.08
Silicon, Si (％): 0.10 ~ 0.80
Manganese, Mn (％): 1.25 ~ 2.00
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 12.0 ~ 15.0
Nickel, Ni (％): 24.0 ~ 28.0
Molybdenum, Mo (％): 1.25 ~ 2.25
Nitrogen, N (&): -
Others (％): Copper ≤ 0.25, Aluminum ≤ 0.25, Titanium 2.70 ~ 3.30, Boron 0.01 ~ 0.07
MECHANICAL PROPERTIES AT ROOM TEMP.
Condition: solution treated at 815 ℃.and then at 480°C for 2h in air
Tensile strength, Rm / MPa: 1400MPa
Yield strength, Rp 0.2 / MPa: 1205 MPa
Elongation, A (％): 10.0
Reduction of area, Z (％): -
Hardness under heat treatment condition | HBW 352 ~ 432
Condition: solution treated at 815 ℃.and then at 480°C for 2h in air
Tensile strength, Rm / MPa: 1400MPa
Yield strength, Rp 0.2 / MPa: 1205 MPa
Elongation, A (％): 10.0
Reduction of area, Z (％): -
Hardness under heat treatment condition | HBW 352 ~ 432
RELEVANT STANDARDS FOR REFERENCE
MAM 2241 Tolerances, Metric, Corrosion and Heat Resistant Steel, Iron Alloy, Titanium, and Titanium Alloy Bars and Wire
AMS 2248 Chemical Check Analysis Limits, Corrosion and Heat Resistant Steels and Alloys, Maraging and Other Highly-Alloyed Steels, and Iron Alloys
AMS 2371 Quality Assurance Sampling and Testing, Corrosion and Heat Resistant Steels and Alloys, Wrought Products and Forging Stock.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. This wire has been used typically for screening and stitching applications requiring good corrosion resistance and which may be subjected to elevated temperatures during fabrication or in service
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring both corrosion and oxidation resistance.
PRODUCT PROFILES & DIMENSIONS
Round bar & Disc (diameter): 5.5 to 800mm
Wire rod (diameter): 1.0 ~ 12.5mm
Square bar / Flat bar (Thickness X Width): 10 to 600mm
Length: fixed length, random length, or based on the customer's special requirement.
Round bar & Disc (diameter): 5.5 to 800mm
Wire rod (diameter): 1.0 ~ 12.5mm
Square bar / Flat bar (Thickness X Width): 10 to 600mm
Length: fixed length, random length, or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE & SERVICE
If you are interested in our products or services, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
Hot search：
Previous page：45CrNi
Last page：0Cr19Ni13Mo3