1.3934 is a high Expansion 13.0Nickel - 3.0Chromium - 5.0Managese Nonmagnetic Austenitic Steel, Fastener material, Z50NMC12 Round bar, Flat bar and forgings available
TECHNICAL DATA SHEET - WS 1.3934
Material category - Aerospace material steel series
Techncial specifications (reference) - AMS 5624E
Melting process way - EF + AOD + ESR
Customs HS code - 72221100 / 72221900 / 72223000
Stock available: diameter 15 ~ 30mm.
Material category - Aerospace material steel series
Techncial specifications (reference) - AMS 5624E
Melting process way - EF + AOD + ESR
Customs HS code - 72221100 / 72221900 / 72223000
Stock available: diameter 15 ~ 30mm.
TYPICAL CHEMICAL ELEMENTS (mass weight - %)
Carbon, C (％): 0.50 ~ 0.70
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 3.50 ~ 5.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 3.00 ~ 5.00
Nickel, Ni (％): 11.0 ~ 14.0
Molibdenum, Mo (%): ≤ 0.50
Copper, Cu (％): ≤ 0.50
Carbon, C (％): 0.50 ~ 0.70
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 3.50 ~ 5.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 3.00 ~ 5.00
Nickel, Ni (％): 11.0 ~ 14.0
Molibdenum, Mo (%): ≤ 0.50
Copper, Cu (％): ≤ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Heat treatment condition: 1010 ~ 1050 ℃, water or oil cooled
Tensile strength, Rm / MPa: 620 min.
Yield strength, Rp0.2 / MPa: -
Elongation, A5 (％): 40.0
Reduction of area, ф (％): -
Hardness solution condition | HBW: 289 max.
Heat treatment condition: 1010 ~ 1050 ℃, water or oil cooled
Tensile strength, Rm / MPa: 620 min.
Yield strength, Rp0.2 / MPa: -
Elongation, A5 (％): 40.0
Reduction of area, ф (％): -
Hardness solution condition | HBW: 289 max.
PROFILE & DIMENSIONS AVAILABLE
Rod / round bar & disc (diameter): 5.5mm to 800mm
Square bar / flat bar (thickness X width): 10mm ~ 300mm X 15 ~ 550mm
Plate ( forging): T30 ~ 300 * W40 ~ 600 * Lmm
Rod / round bar & disc (diameter): 5.5mm to 800mm
Square bar / flat bar (thickness X width): 10mm ~ 300mm X 15 ~ 550mm
Plate ( forging): T30 ~ 300 * W40 ~ 600 * Lmm
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.