1.4945
2014-09-14 08:34:56 Origin： Remark：0 Click：
Descriptions 1.4945 datasheet, 1.4945 Chemical, 1.4945 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL SPECIFICATION - W-Nr 1.4945
MATERIAL CATEGORY - High temperature high strength steel and superalloy
PRODUCT DESCRIPTION
The alloy is usually produced by AOD/VIM/VOD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
MATERIAL SPECIFICATIONS - DIN 17742, 17460, 17480 (2002/1992), DIN EN 103021, 10296, 10095
AVAILABLE SHAPES
Round bar / flat bar / square bar / ring / forge tube
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.04～0.10
Si (％): 0.30～0.60
Mn (％): ≤1.50
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 15.5～17.5
Ni (％): 15.5～17.5
Mo (％): -
W (％): 2.50～3.50
Si (％): 0.30～0.60
Mn (％): ≤1.50
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 15.5～17.5
Ni (％): 15.5～17.5
Mo (％): -
W (％): 2.50～3.50
Nb+Ta (%): 10×C ~ 1.20
N (%): ≤ 0.10
Hot forming temperature /℃: 1150～850
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1100~1150 air/ oil
Heat treatment temperature /℃ | tempering: 750~800
Heat treatment temperature /℃ | ageing: -
Condition: solution treatment
Mechanical property under room temperature |σb/MPa: 540~ 740
Mechanical property under room temperature |σs≥/MPa: 255
Mechanical property under room temperature |δ5≥(％): 30
Mechanical property under room temperature |Akv(DVM): 69
Heat stability temperature/℃: -
Non-scale temperature in air /℃: 650
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|200: 196
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 177
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 167
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 157
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 147
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 177
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 167
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 157
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 147
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|600: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 236
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 93
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: 36
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 162
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 236
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 93
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: 36
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 162
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|700: 54
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
INVENTORY - Forged bar, disc
Diameter: 230mm, 212mm
Quantity: 1010kg
Diameter: 230mm, 212mm
Quantity: 1010kg
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to email or call our resident team of qualified production engineers, Email: sales@ccsteels.com