Descriptions 2.4631 datasheet, 2.4631 Chemical, 2.4631 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL DATASHEET - AMS 2.4631
MATERIAL CATEGORY - High temperature high strength steel and superalloy
MATERIAL SPECIFICATIONS - DIN 17742, 17460, 17480, DIN EN 103021, 10296, 10095
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.04 ~ 0.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 18.0 ~ 21.0
Ni (％): ≥ 65.0
Mo (％): -
Al (％): 1.00 ~ 1.80
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 18.0 ~ 21.0
Ni (％): ≥ 65.0
Mo (％): -
Al (％): 1.00 ~ 1.80
Ti (%): 1.80 ~ 2.70
Others (%): Co ≤2.00, B ≤0.008, Fe ≤3.0, Cu ≤0.20
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃: 1150～1050
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1065~1080 air
Heat treatment temperature /℃ | tempering: 835~865
Heat treatment temperature /℃ | ageing: 685~715
Condition: precipitation hardening
Mechanical property under room temperature |σb/MPa: ≥980
Mechanical property under room temperature |σs≥/MPa: 590
Mechanical property under room temperature |δ5≥(％): 12
Mechanical property under room temperature |Akv(DVM): 17
Heat stability temperature/℃: 700
Non-scale temperature in air /℃: 950
PRODUCT DESCRIPTION
The alloy is usually produced by AOD/VIM/VOD followed by electroslag refining (ESR) or VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
AVAILABLE SHAPES
Round bar / flat bar / square bar / valve body / strip
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing /discs /shaft
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 350mm
Square bar / Flat bar: 3mm to 800mm
Plate / Sheet steel / Steel strip: 0.1mm to 800mm
Width: 8mm to 800mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.