X5NiCrAlTi31-20
2014-09-15 09:25:14 Origin： Remark：0 Click：
Description X5NiCrAlTi31-20 datasheet, X5NiCrAlTi31-20 Chemical, X5NiCrAlTi31-20 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - DIN X5NiCrAlTi31-20
MATERIAL CATEGORY - High temperature high strength steel and superalloy
MATERIAL SPECIFICATIONS - DIN 17742, 17460, 17480, DIN EN 103021, 10296, 10095
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.03 ~ 0.08
Si (％): ≤ 0.70
Mn (％): ≤ 1.50
P (％)≤: 0.015
S (％)≤: 0.010
Cr (％): 19.0 ~ 22.0
Ni (％): 30.0 ~ 32.5
Mo (％): -
Al (％): 0.20 ~ 0.50
Si (％): ≤ 0.70
Mn (％): ≤ 1.50
P (％)≤: 0.015
S (％)≤: 0.010
Cr (％): 19.0 ~ 22.0
Ni (％): 30.0 ~ 32.5
Mo (％): -
Al (％): 0.20 ~ 0.50
Ti (%): 0.20 ~ 0.50
Others (%): Co ≤0.50，Nb ≤0.10，Cu ≤0.50，N ≤0.030
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃: 1150～750
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1100~1200 air/water
Heat treatment temperature /℃ | tempering: -
Heat treatment temperature /℃ | ageing: -
Condition: solution treatment
Mechanical property under room temperature |σb/MPa: 500 ~ 700
Mechanical property under room temperature |σs≥/MPa: 170
Mechanical property under room temperature |δ5≥(％): 35
Mechanical property under room temperature |Akv(DVM): -
Heat stability temperature/℃: -
Non-scale temperature in air /℃: -
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|200: 116
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 95
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 85
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 80
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 75
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: 75
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: 70
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 95
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 85
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 80
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 75
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: 75
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: 70
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|600: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 140
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 69
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: 70
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 95
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 140
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 69
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: 70
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 95
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|700: 44
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD/VIM/VOD followed by electroslag refining (ESR) or VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
AVAILABLE SHAPES
Round bar / flat bar / square bar / valve body / strip
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing / discs / shaft
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE