ISO 4597 - 2001. of Steel 1.2103 Round bar, Plate, Forging Bar & Plate machined, DIN 1.2103 Alloy Exporters Stock sale.
DIN 58SiCr8 & W-Nr 1.2103 - DATA SHEET
Material category: Cold work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.55 ~ 0.63
Silicon, Si (％): 1.70 ~ 2.00
Manganese, Mn (％): 0.60 ~ 0.90
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.035
Chromium, Cr (％): 0.35 ~ 0.45
Molybdenum, Mo (％): -
Vanadium, V (％): -
Silicon, Si (％): 1.70 ~ 2.00
Manganese, Mn (％): 0.60 ~ 0.90
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.035
Chromium, Cr (％): 0.35 ~ 0.45
Molybdenum, Mo (％): -
Vanadium, V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 700～720
Hardness after annealing ≤HBW: 230
Annealing temperature /℃: 700～720
Hardness after annealing ≤HBW: 230
Quenching temperature /℃: 840～850
Cooling medium: water / oil
Common tempering temperature /℃: 400~500
Hardness after tempering at temperature HRC|100℃: 57
Hardness after tempering at temperature HRC|200℃: 54
Hardness after tempering at temperature HRC|300℃: 50
Hardness after tempering at temperature HRC|400℃: 45
Cooling medium: water / oil
Common tempering temperature /℃: 400~500
Hardness after tempering at temperature HRC|100℃: 57
Hardness after tempering at temperature HRC|200℃: 54
Hardness after tempering at temperature HRC|300℃: 50
Hardness after tempering at temperature HRC|400℃: 45
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 500mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Hot search：1.2103