105MnCr4
2014-09-17 09:45:01 Origin： Remark：0 Click：
Specifications 105MnCr4 datasheet, 105MnCr4 Forging Bar, 105MnCr4 Steel exporters. Technical Specifications - EN ISO 4957: 2000. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
ALLOY TOOL STEEL DATASHEET - DIN 105MnCr4
MATERIAL CATEGORY - Cold work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / BEF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 1.00 ~ 1.10
Si (％): 0.15 ~ 0.30
Mn (％): 1.00 ~ 1.20
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.70 ~ 1.00
Mo (％): -
V (％): -
Si (％): 0.15 ~ 0.30
Mn (％): 1.00 ~ 1.20
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.70 ~ 1.00
Mo (％): -
V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 680～720
Hardness after annealing ≤HBW: 220
Annealing temperature /℃: 680～720
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 800～860
Cooling medium: water / oil
Common tempering temperature /℃: 180~250
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 62
Hardness after tempering at temperature HRC|300℃: 57
Hardness after tempering at temperature HRC|400℃: --
Cooling medium: water / oil
Common tempering temperature /℃: 180~250
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 62
Hardness after tempering at temperature HRC|300℃: 57
Hardness after tempering at temperature HRC|400℃: --
AVAILABLE SHAPES
Round bar / flat bar / square bar / plate / forge piece
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 400mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to email or call our resident team of qualified production engineers. E-mail sales@ccsteels.com