Specifications 1.2162 Suppliers, Stocklist 1.2162 Datasheet, Inventory 1.2162 Forging Bar plate machined, Steel exporters. Technical Specifications - EN ISO 4957: 2000. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TOOL STEEL DATA SHEET - DIN 1.2162
MATERIAL CATEGORY - Cold work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / BEF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
AVAILABLE SHAPES
Round bar / flat bar / square bar / plate / valve / ring
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.18 ~ 0.24
Si (％): 0.15 ~ 0.35
Mn (％): 1.10 ~ 1.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.00 ~ 1.30
Mo (％): -
V (％): -
Si (％): 0.15 ~ 0.35
Mn (％): 1.10 ~ 1.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.00 ~ 1.30
Mo (％): -
V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 680～710
Hardness after annealing ≤HBW: 215
Annealing temperature /℃: 680～710
Hardness after annealing ≤HBW: 215
Quenching temperature /℃: 810～840
Cooling medium: water / oil
Common tempering temperature /℃: 150~180
Hardness after tempering at temperature HRC|100℃: 61 surface hardness
Hardness after tempering at temperature HRC|200℃: 60 surface hardness
Hardness after tempering at temperature HRC|300℃: 57 surface hardness
Hardness after tempering at temperature HRC|400℃: 54 surface hardness
Cooling medium: water / oil
Common tempering temperature /℃: 150~180
Hardness after tempering at temperature HRC|100℃: 61 surface hardness
Hardness after tempering at temperature HRC|200℃: 60 surface hardness
Hardness after tempering at temperature HRC|300℃: 57 surface hardness
Hardness after tempering at temperature HRC|400℃: 54 surface hardness
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 500mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.